Abstract The work was to develop novel high temperature microwave absorbing material based MgZr4(PO4)6 (MZP) ceramic. The results show that thermal expansion process at higher temperature expand along c-axis while… Click to show full abstract
Abstract The work was to develop novel high temperature microwave absorbing material based MgZr4(PO4)6 (MZP) ceramic. The results show that thermal expansion process at higher temperature expand along c-axis while shrink along the a-axis. The conductivity of MZP ceramic was increased by 1000 orders due to the increase in magnesium ion mobility. In addition, the results indicates that the dielectric properties were dependent on temperature at all measured frequencies. The real and imaginary parts of dielectric constant increased from 4.0–5.2 and 0.024 to 0.4, respectively. The reflection loss varied with the change in thickness and the minimum reflection loss value was -26.66 dB at 800℃, suggesting that MZP ceramic was a promising novel high temperature microwave absorbing material.
               
Click one of the above tabs to view related content.