Abstract HfC-TaC/HfC-SiC alternate coatings with different sublayer thicknesses were fabricated on SiC-coated carbon/carbon composites by supersonic atmosphere plasma spraying. Their ablation resistance was studied under oxyacetylene torch and compared with… Click to show full abstract
Abstract HfC-TaC/HfC-SiC alternate coatings with different sublayer thicknesses were fabricated on SiC-coated carbon/carbon composites by supersonic atmosphere plasma spraying. Their ablation resistance was studied under oxyacetylene torch and compared with monolayered HfC-TaC coating. The alternate coating with 6 spray cycles of HfC-TaC and 3 spray cycles of HfC-SiC sublayers exhibited the best ablation performance as confirmed by the integral coating morphology and the lowest ablation rates. A dense oxide layer acting as an oxygen insulator and the release of thermal stress induced by the formation of dendritic cracks are thought to be responsible for its great ablation resistance. For the alternate coating with 4 spray cycles of HfC-TaC and 2 spray cycles of HfC-SiC sublayers, exfoliation occurred at the interface of two adjacent sublayers, leading to violent evaporation of exposed HfC-SiC sublayer.