Abstract In this study, 10 μm-thick TiO2 nanotube arrays (TNAs) coated with a MoO3 layer were prepared by electrochemical oxidation on titanium foil followed by successive cyclic voltammetric deposition, aiming at the fabrication of a thick binder-free anode with high capacity and good cycling stability for lithium ion batteries (LIBs). Through the evaluation of the electrochemical performance of electrodes prepared under various conditions, the electrode obtained at a precursor concentration of 5 mM showed the best electrochemical performance, exhibiting high reversible capacity and enhanced cycling stability. With the structural advantage and intrinsic characteristics of TNAs, the large volume expansion of MoO3 is successfully accommodated, resulting in 97% retention at a rate of 5 C over 500 cycles and 91% retention even at a high rate of 25 C.