LAUSR

Abstract Manganese ferrites (MnFe 2 O 4 ) have been of great interest for their remarkable and soft-magnetic properties (low coercivity, moderate saturation magnetization) accompanied by good chemical stability and mechanical hardness. X-ray diffraction analysis confirmed the presence of single phase cubic spinel ferrite with space group Fm3m for all prepared samples. Structural parameters such as lattice constant, crystallite size were calculated from the studies of X-ray diffraction. The morphological analysis of all the compounds is studied using scanning electron microscope. The magnetic properties were measured using electron spin resonance (ESR) and vibrating sample magnetometer (VSM). The results obtained showed the formation of manganese ferrites with an average particle size are in good agreement with previous results and displayed good magnetic properties. The dielectric and impedance properties are studied over a frequency range 20 Hz–1 MHz at room temperature.