Abstract In this work, room temperature magnetoelectric properties of (0−3) particulate composites of non lead based piezoelectric BNTKNNLTS [0.97(Bi 0.5 Na 0.5 TiO 3 )–0.03(K 0.47 Na 0.47 Li 0.06 Nb 0.74 Sb 0.06 Ta 0.2 O 3 ) and magnetostrictive CZFMO (Co 0.6 Zn 0.4 Fe 1.7 Mn 0.3 O 4 ) are presented. Composite samples of (1- x )(BNTKNNLTS)- x (CZFMO) , with x =0.1 and 0.5, are synthesized by solid state reaction route. X-ray diffraction confirms the single phase formation of parent phases and the presence of two phases in the composites. Similar sintering conditions of the two individual components lead to optimal ferroelectric and ferromagnetic properties in the composites. A large self-biased magnetoelectric (ME) coupling ~74 mV/cm.Oe for the sample with x =0.1 (measured in longitudinally magnetized-transversely polarized configuration) is observed at room temperature.