LAUSR

Abstract High coercivity of hot-deformed Nd 2 Fe 14 B magnets was obtained by grain boundary diffusion. Comparable squareness and similar magnetic properties for samples diffusing from side and pole surfaces show little discrepancies if quantities of the infiltrated PrNd-Cu low eutectic alloys is enough to obtain sufficient diffusion. However, the microstructures and higher characteristic peak ratios show preferable orientation of grains near surfaces of the sample diffused from side surfaces than that from pole surfaces. Amorphous Nd-rich phases and crystal Fe-rich phases were both observed in the diffused magnets. The enhancement of coercivity is considered to be resulted from grain boundary optimization and magnetic isolation which is caused by the thickened nonmagnetic intergranular phases.