Abstract Li-doped In2O3 nanoparticles with room temperature d0 ferromagnetism were prepared by a sol-gel method. X-ray diffraction, X-ray photoelectron spectroscopy and photoluminescence were carried out to investigate the effects of Li incorporation on the lattice defects. As the content of Li increases, non-monotonic changes in shifts of XRD peak (2 2 2) and the intensity ratios of indium vacancies related photoluminescence peak (PII) with respect to oxygen vacancies related peak (PI) are observed. Results show that at low doping level (≤2 at.%) Li prefers to occupy In sites, while with further doping the interstitial sites are more favorable for Li. Combined with the consistent non-monotonic change in saturation magnetization, we think that indium vacancies resulting from Li-doping play an important role in inducing d0 ferromagnetism in our Li-doped In2O3 nanoparticles, and the FM coupling is mainly mediated by the LiIn-ONN-VIn-ONN-LiIn chains.