We report on the static and dynamic magnetic properties of W/CoFeB/Ta/CoFeB/MgO stacks, where the CoFeB layer is split in two by a 0.3 nm-thick Ta "dusting" layer. A total CoFeB thickness between 1.2 and 2.4 nm is studied. Perpendicular magnetic anisotropy is obtained for thickness below 1.8 nm even at the as-deposited stacks, and it is enhanced after annealing. Saturation magnetization is 1520 (1440) kA/m before (after) annealing, increased compared to non-split CoFeB layers. Ferromagnetic resonance measurements show that high magnetic anisotropy energy may be achieved (effective anisotropy field 0.571 ± 0.003 T), combined to a moderate Gilbert damping (0.030 ± 0.001). We argue that the above characteristics make the split-CoFeB system advantageous for spintronics applications.