LAUSR

Abstract U3Si2 and U3Si5 are two important uranium silicide phases currently under extensive investigation as potential fuel forms or components for light water reactors (LWRs) to enhance accident tolerance. In this paper, their irradiation behaviors are studied by ion beam irradiations with various ion mass and energies, and their microstructure evolution is investigated by in-situ transmission electron microscopy (TEM). U3Si2 can easily be amorphized by ion beam irradiations (by 1 MeV Ar2+ or Kr2+) at room temperature with the critical amorphization dose less than 1 dpa. The critical amorphization temperatures of U3Si2 irradiated by 1 MeV Kr2+ and 1 MeV Ar2+ ion are determined as 580 ± 10 K and 540 ± 5 K, respectively. In contrast, U3Si5 remains crystalline up to 8 dpa at room temperature and is stable against ion irradiation-induced amorphization up to ∼50 dpa by either 1 MeV Kr2+ or 150 KeV Kr+ at 623 K. These results provide valuable experimental data to guide future irradiation experiments, support the relevant post irradiation examination, and serve as the experimental basis for the validation of advanced fuel performance models.