INTRODUCTION This study aimed to investigate dental pulp responses to novel bioactive glass (BG) pulp capping materials after direct pulp capping in vivo. METHODS Novel BG pulp capping materials are composed… Click to show full abstract
INTRODUCTION This study aimed to investigate dental pulp responses to novel bioactive glass (BG) pulp capping materials after direct pulp capping in vivo. METHODS Novel BG pulp capping materials are composed of powder and fluid. The powder is BG (82.36% SiO2, 15.36% CaO, and 2.28% P2O5), and the fluid is provided in 2 kinds: (1) phosphate buffer solution (BG-PB) and (2) phosphate buffer solution with the addition of 1 wt% sodium alginate (BG-PB-SA). After mixing the powder and fluid, BG-PB and BG-PB-SA were prepared. Cavities with mechanical pulp exposure were prepared on maxillary first molars of Wistar rats. The exposures were randomly capped with BG-PB, BG-PB-SA, or mineral trioxide aggregate (MTA). After 1 (n = 6) and 4 weeks (n = 8), maxillary segments were obtained and prepared for histologic analysis with a scoring system. Statistical analysis was performed using the Kruskal-Wallis and Mann-Whitney U tests with the significance set at .05. RESULTS After 1 week, few inflammatory cells were present in the BG-PB, BG-PB-SA, and MTA groups. Moreover, a thin layer of newly generated matrix was observed in most specimens. After 4 weeks, all specimens from the 3 groups formed a heavy dentin bridge. BG-PB and BG-PB-SA groups exhibited no or slight inflammatory response, whereas the MTA group exhibited a slight to moderate inflammatory response. No significant difference was observed in pulp inflammation and dentin formation among the 3 groups at either time point (P > .05). CONCLUSIONS When used as a pulp capping agent, BG-PB and BG-PB-SA had similar favorable cellular and inflammatory pulp responses to those of MTA. Therefore, BG is a promising pulp capping material.
               
Click one of the above tabs to view related content.