Abstract Structure and mechanical properties of Zn–Fe–Mo coatings deposited on AISI 1015 at constant current were investigated. It has been shown that with increasing cathodic current density from 5 to 30 mA cm−2… Click to show full abstract
Abstract Structure and mechanical properties of Zn–Fe–Mo coatings deposited on AISI 1015 at constant current were investigated. It has been shown that with increasing cathodic current density from 5 to 30 mA cm−2 molybdenum content in the coatings was almost constant and close to 1.5 at.%, while the content of iron reached a minimum (3.2 at.%) at 15 mA cm−2. Uniform coatings characterized by low roughness (Ra and Sa
               