Abstract We report on the structure and surface composition of Nd0.33Eu0.67Fe1-xCrxO3 (x = 0.0, 0.3, 0.5, 0.7, 0.9 and 1.0) nanoparticles (∼30 nm) mechanosynthesized at temperatures that are ∼ 470–700 °C lower than those at which the pure and doped pristine materials conventionally form. XRD Rietveld and FT-IR analyses show that with increasing x the lattice parameters decrease and the bond lengths and angles vary in a way that reduces crystalline distortion. Whilst the majority of the Eu3+/Nd3+ and Fe3+/Cr3+ cations occupy their normal perovskite-related A- and B-sites, respectively, ∼ 5 % of them exchange sites. 57Fe Mossbauer spectroscopy favours the presence of these antisites and reveals a superparamagnetic behaviour at 298 K that enhances with increasing x. XPS measurement reveals a complex surface composition of the nanoparticles with traces of Eu2O3, Nd2O3, Cr2O3 and Fe2O3 as well as partial O2−-deficiency.