LAUSR

Abstract The catalytic degradation of high density polyethylene (HDPE) was studied in the presence of HZSM-12 zeolites with different Si/Al ratio, by thermogravimetry and pyrolysis coupled to gas chromatography and mass spectrometry. The NaZSM-12 zeolite was synthesized by the hydrothermal method using methyltriethylammonium chloride as template. The HZSM-5 was obtained by ion exchange of NaZSM-12 with ammonium chloride, drying and subsequent calcination. The materials characterization were carried out by chemical analysis, X-ray diffraction, scanning electron microscopy, BET measurements and acidity by n-butylamine adsorption. The obtained HZSM-12 zeolites were physically mixed with HDPE in the proportion of 50%wt and submitted to thermogravimetric analyses at heating rates of 2.5; 5; 10 and 20 °C min −1 . The addition of HZSM-12 to HDPE produced a decreasing in the temperature of polymer degradation, which was proportional to the zeolite acidity. The activation energy (Ea) for the process was determined from the non-isothermal model-free kinetic model proposed by Vyazovkin. The Ea decreases linearly with the concentration of acid sites on the HZSM-12 materials. From the pyrolysis data, the obtained products were typically light gases (C 2 -C 3 ); liquid petroleum gases (C 4 -C 5 ); and gasoline (C 6 -C 10 ). This results suggest that acid zeolites are excellent materials for obtaining alternative fuels from catalytic recycling of plastics.