Pressure leaching of wolframite using a sulfuric-phosphoric acid mixture

Photo by sharonmccutcheon from unsplash

Abstract In this paper, tungsten was extracted from wolframite using sulfuric-phosphoric acid mixtures. During leaching, wolframite was decomposed under acidic conditions, and phosphotungsten heteropoly acid was formed by the complexation… Click to show full abstract

Abstract In this paper, tungsten was extracted from wolframite using sulfuric-phosphoric acid mixtures. During leaching, wolframite was decomposed under acidic conditions, and phosphotungsten heteropoly acid was formed by the complexation of tungsten and phosphorus. The XRD results showed that after wolframite leaching, the residue contained unleached wolframite, quartz, small amounts of calcium sulfate (anhydrite) and phosphotungstate salts. When the concentration of H2SO4 was 2.5 mol/L, the concentration of H3PO4 was 2.0 mol/L, the liquid–solid ratio was 10 mL/g, the reaction time was 4 h, and the reaction temperature was 140 ℃, the maximum leaching efficiency of tungsten reached 98.8%. This method broadens the applicability of the sulfuric-phosphoric mixed acid system to the decomposition of wolframite under pressure hydrometallurgical conditions.

Keywords: wolframite using; phosphoric acid; leaching wolframite; using sulfuric; acid; sulfuric phosphoric

Journal Title: Minerals Engineering
Year Published: 2021

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.