LAUSR

Abstract Organic coatings are the single most widely applied materials to protect metallic substrates against corrosion. Therefore it is important to understand how a coating can guarantee the protective performance during service life. In this study it is tried to find how viscoelastic properties can affect the protective performance of a coating. An epoxy resin (Araldite GY 783) was cured with a mixture of two types of hardeners (a polyether polyamine and a cycloaliphatic polyamine) in four different mixing ratios (i.e. 20–80, 50–50, 70–30, 90–10) to achieve various adhesion behaviors, water permeability and viscoelastic properties. Samples were exposed to humidity in testing chamber for 300 days and adhesion was measured at wet and dry conditions over time. After drying, adhesion loss and recovery were evaluated by pull-off test. Electrochemical behavior of coatings was studied by electrochemical impedance spectroscopy (EIS). A series of impedance spectra of coatings during exposure to humidity were recorded and their protective properties were compared. The results showed a correlation between protective properties and viscoelastic behavior of coatings. It was found that a sample with higher percentage of cycloaliphatic hardener has higher elastic modulus (1275 MPa) and a sample with higher percentage of polyether poly amine hardener has the lower elastic modulus (465 MPa). Additionally It was found that a sample with excellent initial protective properties (|Z| = 10 10  Ω cm 2 ), higher elastic modulus and low initial water permeability (0.308 g/m 2 hr) may quickly fail because of the adhesion failure after wet cycles.