LAUSR

Abstract Three unsaturated compounds bearing respectively phosphate, aryl bromide and sulfenamide moieties were used as flame retardants (FR) for flax fabrics. Due to the presence of carbon-carbon double bonds, radiation-grafting was considered to covalently bond these FR onto fiber structure. Grafting efficiency and location of FR molecules were investigated by weight measurements and SEM-EDX observations. Flammability and especially self-extinguishment were assessed by thermogravimetric analysis, pyrolysis-combustion flow calorimetry and a non-standardized fire test already used in previous studies. All FRs were able to diffuse into elementary fiber bulk. Nevertheless only the phosphonated monomer (noted FR-P) was significantly grafted onto flax. Self-extinguishment was obtained for fabrics containing at least around 0.5 wt% of phosphorus. On the contrary the FR content of flax fibers after radiation-grafting procedure and washing was negligible for FR-S and FR-Br, evidencing that these molecules have not been grafted upon irradiation. Moreover, the combination of these molecules prevents the radiation-grafting of other molecules which showed good grafting rate when used alone.