Abstract Two kinds of Sm(Co bal Fe 0.1 Cu 0.09 Zr 0.03 ) 7.24 high temperature magnets were fabricated by a traditional powder metallurgical technology with different annealing processes. A… Click to show full abstract
Abstract Two kinds of Sm(Co bal Fe 0.1 Cu 0.09 Zr 0.03 ) 7.24 high temperature magnets were fabricated by a traditional powder metallurgical technology with different annealing processes. A record of maximum energy product of 94.73 kJ/m 3 at 773 K with a high intrinsic coercivity of 652.72 kA/m was made. Based on the theoretical and experimental results, it was found that the temperature coefficient of the coercivity was strongly influenced by the variation of the Curie temperature of the cell wall phases and the domain wall energy ratio between cell and cell wall phases at 0 K. The characteristic properties originate from the element redistribution between SmCo 5 /Sm 2 Co 17 interfaces while annealing.
Journal Title: Scripta Materialia
Year Published: 2017
Link to full text (if available)
Share on Social Media: Sign Up to like & get
recommendations!