LAUSR

Abstract The microstructure in a multifunctional β-titanium alloy, Ti–24Nb–4Zr–8Sn (wt%), before and after cold rolling was investigated using conventional and aberration-corrected scanning/transmission electron microscopy. With the presence of nano-scaled orthorhombic phase (O′) and hexagonal phase (ω), primary {332} β deformation twins were activated during cold rolling with a thin layer of orthorhombic martensite (α″) occupying every twin boundary. In the interior of primary twins, nano-scaled α″ particles were observed, together with secondary {112} β twins. Our work may indicate that the pre-formed nano-scaled O′ phase assists in activating the {332} β deformation twining and O′ phase transforms to nano-scaled stress-induced α″ during cold rolling.