Control Al/Mg intermetallic compound formation during ultrasonic-assisted soldering Mg to Al.

Photo by kumpan_electric from unsplash

To prevent the formation of Al/Mg intermetallic compounds (IMCs) of Al3Mg2 and Al12Mg17, dissimilar Al/Mg were ultrasonic-assisted soldered using Sn-based filler metals. A new IMC of Mg2Sn formed in the… Click to show full abstract

To prevent the formation of Al/Mg intermetallic compounds (IMCs) of Al3Mg2 and Al12Mg17, dissimilar Al/Mg were ultrasonic-assisted soldered using Sn-based filler metals. A new IMC of Mg2Sn formed in the soldered joints during this process and it was prone to crack at large thickness. The thickness of Mg2Sn was reduced to 22 μm at 285 °C when using Sn-3Cu as the filler metal. Cracks were still observed inside the blocky Mg2Sn. The thickness of Mg2Sn was significantly reduced when using Sn-9Zn as the filler metal. A 17 μm Mg2Sn layer without crack was obtained at a temperature of 200 °C, ultrasonic power of Mode I, and ultrasonic time of 2 s. The shear strengths of the joints using Sn-9Zn was much higher than those using Sn-3Cu because of the thinner Mg2Sn layer in the former joints. Sn whiskers were prevented by using Sn-9Zn. A cavitation model during ultrasonic assisted soldering was proposed.

Keywords: assisted soldering; control intermetallic; using 9zn; formation; mg2sn; ultrasonic assisted

Journal Title: Ultrasonics sonochemistry
Year Published: 2018

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.