LAUSR

The purpose of the present study was to prepare Orodispersible films (ODFs) loaded with ketoprofen nanoparticles (KT-NP). The Box-Behnken design was constructed in developing and optimizing the KTF-NP-ODFs. The effect of independent variables: Soluplus® concentration (X1, stabilizer), Tween 80 concentration (X2, surfactant), and KTF concentration (X3, drug) were studied on the dependent variables: particle size (PS, Y1), zeta potential (ZP, Y2), and the polydispersity index (PDI, Y3) of the NPs, as well as on the tensile strength (TS, Y4) and permeability coefficient (PC, Y5) of the KTF-NP-ODFs. Hydroxypropyl methylcellulose (HPMC E15) and polyethylene glycol (PEG 400) were used as the film former polymer and plasticizer, respectively, and their concentrations were kept constant for all formulations. KTF-NPs were prepared by antisolvent precipitation technology. This was followed by the addition of HPMC E15 and PEG 400 to prepare the ODFs using the solvent-casting method. The PS, PDI, and ZP for all the formulations were found in the range of 94 nm to 350 nm, 0.09 to 0.438, and -21.83 mV to -8.03 mV, respectively. The TS and PC of the prepared KTF-NP-ODFs were found between 1.21 MPa to 3.93 MPa and 3.12 × 10-4 cm/h to 34.23 × 10-4 cm/h, respectively. The amorphous nature of the KTF-NP in the ODFs was confirmed by the absence of characteristic crystalline peaks and endothermic events of KTF in X-ray diffraction (XRD) and modulated differential scanning calorimetry (mDSC), respectively. The optimized formulation showed ̴ 4 times higher permeability as compared to the pure KTF. In addition, the dissolution of pure KTF and the optimized KTF-NP-ODF in pH 1.2 at the end of 60 min was found to be ̴ 30% and ̴ 95 %, respectively. Conclusively, KTF-NP-ODFs can be a promising drug delivery system to counter the issues related to dysphagia and bypass the common side effects, such as the gastric irritation associated with NSAIDs like KTF.