Reexamining the Crystallization of Poly(ε-caprolactone) and Isotactic Polypropylene under Hard Confinement: Nucleation and Orientation

Photo by palivo_duracka from unsplash

The crystallization of poly(e-caprolactone) (PCL) and isotactic polypropylene (iPP) infiltrated in nanoporous anodic alumina oxide (AAO) templates was reexamined to demonstrate the importance of obtaining polymer-free, clean AAO surfaces on… Click to show full abstract

The crystallization of poly(e-caprolactone) (PCL) and isotactic polypropylene (iPP) infiltrated in nanoporous anodic alumina oxide (AAO) templates was reexamined to demonstrate the importance of obtaining polymer-free, clean AAO surfaces on the nucleation, size dependence of crystallization temperature (Tc), and texture. The AAO pore diameters cover a broad range from 400 to 20 nm. When the AAO templates were completely free of any residual polymer on their surfaces, differential scanning calorimetry (DSC) experiments exhibited a single crystallization peak for all the samples with different AAO pore sizes. A drastic decrease in Tc with density of domains indicated a transition from heterogeneous to homogeneous/surface nucleation. A regular decrease of Tc with pore size was observed in the low Tc regime, as a result of the volume dependence of nucleation events. The chain alignment of the two polymers infiltrated in AAO was studied by two-dimensional wide-angle X-ray scattering (WAXS). By comparing the ex...

Keywords: crystallization poly; crystallization; nucleation; poly caprolactone; isotactic polypropylene

Journal Title: Macromolecules
Year Published: 2017

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.