Reduced graphene oxide (rGO) has been prepared from commercial graphene oxide by a thermal reduction method, and NiO/rGO photocathodes were obtained by a mixed NiCl2/rGO sol–gel process by using different amounts of rGO material. A detailed characterization of NiO/rGO films was carried out by SEM, Raman, and surface analysis. BET analysis revealed that the optimum surface area of the films was between 0.0 and 0.3 mg of rGO, while the surface area was lower with increasing graphene content. Despite the lower surface area, in the presence of the higher amount of rGO material, a higher dye uptake was detected, possibly because of a π-staking interaction between the phenyl group of the dye and the graphene sheets. The p-type dye-sensitized solar cells prepared from these films showed a gradual increase in JSC up to 2.6 mA/cm2 with the higher amount of rGO and a VOC of 125 mV; in this case, the efficiency was almost 2 times higher with respect to the solar cell with NiO alone. An EIS study showed that the char...