Inorganic perovskite CsPbBr3 has broad application prospects in photovoltaic windows, tandem cells, and other fields due to its intrinsic semitransparency, excellent photoelectric properties, and stability. In this work, a high-quality semitransparent CsPbBr3 film was prepared by a sequential vacuum evaporation deposition method without high-temperature annealing and successfully used as the active layer of flexible perovskite solar cells (F-PSCs) for the first time, achieving a power conversion efficiency (PCE) of 5.00%. By introducing an energy-level buffer layer of Cu2O between CsPbBr3 and Spiro-OMeTAD, the champion PCE has been further improved to 5.67% owing to the reduction of electron-hole recombination and enhanced charge extraction. The optimized devices present higher stability, which can maintain more than 95% of the initial efficiency even after continuous heating at 85 °C for 240 h. Moreover, the F-PSCs also exhibit excellent mechanical durability, and 90% of the original PCE can be retained after 1000 bending cycles at a curvature radius of 3 mm.