Eco-Friendly Push-Coated Polymer Solar Cells with No Active Material Wastes Yield Power Conversion Efficiencies over 5.5.

Photo from wikipedia

Push-coating is a simple process that can be employed for extremely low-cost polymer electronic device production. Here, we demonstrate its application to the fabrication of poly(2,7-carbazole- alt-dithienylbenzothiadiazole) (PCDTBT):[6,6]-phenyl-C71-butyric acid methyl… Click to show full abstract

Push-coating is a simple process that can be employed for extremely low-cost polymer electronic device production. Here, we demonstrate its application to the fabrication of poly(2,7-carbazole- alt-dithienylbenzothiadiazole) (PCDTBT):[6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) active layers processed in air, yielding similar photovoltaic performances as thermally annealed spin-coated thin films when used in inverted polymer solar cells (PSCs). During push-coating, the polydimethylsiloxane layer temporarily traps the deposition solvent, resulting in simultaneous film formation and solvent annealing effect. This removes the necessity for a postdeposition thermal annealing step which is required for spin-coated PSCs to produce high photovoltaic performances. Optimized PSC active layers are produced with a push-coating time of 5 min at room temperature with 20 times less hazardous solvent and 40 times less active material than spin-coating. Annealed spin-coated active layers and active layers push-coated for 5 min both produce average power conversion efficiencies (PCEs) of 5.77%, while those push-coated for a shorter time of 1 min yield a slightly lower value of 5.59%. We demonstrate that, despite differences in their donor:acceptor vertical concentration gradients, unencapsulated PCDTBT:PC71BM active layers push-coated for 1 min produce PSCs with similar operational stability and upscaling capacity as thermally annealed spin-coated ones. As fast device fabrication can be achieved with short-time push-coating, we further demonstrate the potential of this deposition technique by manufacturing push-coated PSC-based semitransparent photovoltaic devices with a PCE of 4.23%, relatively neutral colors and an average visible transparency of 40.2%. Our work thus confirms that push-coating is not limited to the widely employed poly(3-hexylthiophene-2,5-diyl) but can also be used with low band gap copolymers and opens the path to low-cost and eco-friendly, yet efficient and stable PSCs.

Keywords: push coating; active layers; push coated; spin coated; push; polymer solar

Journal Title: ACS applied materials & interfaces
Year Published: 2019

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.