Photorefractive Response Enhancement in Poly(triarylamine)-Based Polymer Composites by a Second Electron Trap Chromophore

Photo from wikipedia

Photorefractive (PR) performances are affected by the components of the photoconductor, sensitizer, nonlinear optical dye, and plasticizer. A photoconductor with high hole mobility promises a faster response time, whereas it… Click to show full abstract

Photorefractive (PR) performances are affected by the components of the photoconductor, sensitizer, nonlinear optical dye, and plasticizer. A photoconductor with high hole mobility promises a faster response time, whereas it induces higher photoconductivity, which leads to easy dielectric breakdown. Adding a second electron trap is effective in controlling photoconductivity. In this study, the role of a second electron trap 1,3,5-tri[(3-pyridyl)-phen-3-yl]benzene (TmPyPB) was investigated in a PR composite consisting of a photoconductor of poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine] with a high hole mobility, a nonlinear optical chromophore of piperidinodicyanostyrene, a plasticizer of (2,4,6-trimethylphenyl)diphenylamine, and a sensitizer of [6,6]-phenyl C61 butyric acid-methyl ester. The minimum time response with the maximum optical diffraction efficiency and sensitivity was measured at a 1 wt % content of TmPyPB. These results were consistent with the number of charge carriers trapped per unit volume and per unit time Nc (cm–3 s–1), which is defined as the ratio between the initial trap density Ti (cm–3) and response time τ (s), at a 1 wt % content of TmPyPB. A faster response time of 149 μs, optical diffraction of 24.1% (external diffraction of 4.8%), and a sensitivity of 2746 cm2 J–1 were measured at 50 V μm–1 for the sample with 1 wt % TmPyPB. High loading of 5 wt % TmPyPB led to a large decrease in photoconductivity and effectively suppressed the dielectric breakdown under a stronger electric field, whereas a slower response time with lower diffraction efficiency was observed for optical diffraction.

Keywords: electron trap; time; response; second electron

Journal Title: ACS Omega
Year Published: 2022

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.