Synthesis and charge storage properties of templated LaMnO3-SiO2 composite materials.

Photo by trnavskauni from unsplash

Mesoporous LaMnO3 with bulk surface areas in the range 225-300 m2 g-1 were prepared by direct overgrowth around the short-channel version of SBA-15 silica. The extent of LaMnO3 growth was… Click to show full abstract

Mesoporous LaMnO3 with bulk surface areas in the range 225-300 m2 g-1 were prepared by direct overgrowth around the short-channel version of SBA-15 silica. The extent of LaMnO3 growth was found to be affected by the polarity of solvent system used to impregnate the SBA-15 with La3+ and Mn2+ precursors. The resulting LaMnO3-SiO2 composites were stable in refluxing NaOH, suggesting that the SiO2 was fully encapsulated. The composites were structurally characterized using a range of techniques including 2-D elemental mapping and Raman spectroscopy. The electrochemical behavior of the composites was tested for pseudocapacitance, which revealed normalized specific capacitances over 200 F g-1.

Keywords: charge storage; sio2; lamno3 sio2; properties templated; synthesis charge; storage properties

Journal Title: Dalton transactions
Year Published: 2017

Link to full text (if available)


Share on Social Media:                               Sign Up to like & get
recommendations!

Related content

More Information              News              Social Media              Video              Recommended



                Click one of the above tabs to view related content.