Recent reports have suggested that the long decay times in time resolved photoluminescence (TRPL), often measured in Cu(In, Ga)Se2 absorbers, may be a result of detrapping from sub-bandgap defects. In… Click to show full abstract
Recent reports have suggested that the long decay times in time resolved photoluminescence (TRPL), often measured in Cu(In, Ga)Se2 absorbers, may be a result of detrapping from sub-bandgap defects. In this work, we show via temperature dependent measurements, that long lifetimes >50 ns can be observed that reflect the true minority carrier lifetime not related to deep trapping. Temperature dependent time resolved photoluminescence and steady state photoluminescence imaging measurements are used to analyze the effect of annealing in air and in a nitrogen atmosphere between 300 K and 350 K. We show that heating the Cu(In, Ga)Se2 absorber in air can irreversibly decrease the TRPL decay time, likely due to a deterioration of the absorber surface. Annealing in an oxygen-free environment yields a temperature dependence of the TRPL decay times in accordance with Schockley Read Hall recombination kinetics and weakly varying capture cross sections according to T0.6.
               
Click one of the above tabs to view related content.