This paper reports an interesting observation of great differences in the temperature of exploded wires with insulation coating of different thicknesses. Two kinds of polyimide-coated tungsten wires were used with the same conductive diameter 12.5 μm but a different thickness of coating, 0.75–2.25 μm and 2.25–4.25 μm, respectively. The specific energy reconstructed from the current and voltage signals was quite close for the tested wires. However, the exploding scenario, obtained from Mach-Zehnder interferograms, showed great differences: a neutral outer-layer was observed around the thick-coated wire, which was absent for the thin-coated wire; and the calculated electron density and local thermal equilibrium temperature were much higher for thick-coated wires. The heat-preserving neutral layer formed by the decomposition of the insulation was supposed to be the cause of this phenomenon.