In this study, the structural, magnetic, and magneto-transport properties of La1.5Sr0.5CoMnO6 (LSCMO) thin films deposited on a SrTiO3 (001) substrate were investigated. A normal θ/2θ x-ray diffraction, rocking curve, ϕ-scan,… Click to show full abstract
In this study, the structural, magnetic, and magneto-transport properties of La1.5Sr0.5CoMnO6 (LSCMO) thin films deposited on a SrTiO3 (001) substrate were investigated. A normal θ/2θ x-ray diffraction, rocking curve, ϕ-scan, and reciprocal space mapping data showed that prepared LSCMO thin films are single phase and highly strained with epitaxial nature. Temperature vs. magnetization of LSCMO films exhibits strain-induced ferromagnetic ordering with TC ∼ 165 K. In contrast to the bulk samples, there was no exchange bias and canted type antiferromagnetic and spin glass behavior in films having thickness (t) ≤ 26 nm. Temperature dependent resistivity data were explained using Schnakenberg's model and the polaron hopping conduction process. The slope change in resistivity and magnetoresistance maximum (∼65%) around TC indicates the existence of a weak double exchange mechanism between the mixed valence states of transition metal ions. Suppression of spin dependent scattering with the magnetic field is attri...
               
Click one of the above tabs to view related content.