Photocatalytic response of as-quenched and heat-treated 2Bi2O3-B2O3 glasses was studied. X ray diffraction reveals that the controlled heat treatment of glasses at 380 °C for 1 h, 2 h, and 3 h shows the formation of Bi4B2O9 crystals embedded in 2Bi2O3-B2O3 the host glass matrix. Scanning electron microscopic images reveal the presence of nanocrystallization in as-quenched glass. Significant photocatalytic activities were observed in as-quenched transparent glass. Photocatalytic activities were studied using the degradation of Resazurin as well as pharmaceutical 17 β-Estradiol under UV irradiation. Measurement of contact angle shows enhanced hydrophilicity with the increase in crystallization of the samples. Further, for as quenched 2Bi2O3-B2O3 glass ceramic, under UV irradiation, the water contact angle decreased from 92.7° to 39.5° and the sample surface transformed from hydrophobic to hydrophilic. Effective photocatalytic performance along with photoinduced hydrophilicity promotes 2Bi2O3-B2O3 glass ceramics in self-cleaning applications.Photocatalytic response of as-quenched and heat-treated 2Bi2O3-B2O3 glasses was studied. X ray diffraction reveals that the controlled heat treatment of glasses at 380 °C for 1 h, 2 h, and 3 h shows the formation of Bi4B2O9 crystals embedded in 2Bi2O3-B2O3 the host glass matrix. Scanning electron microscopic images reveal the presence of nanocrystallization in as-quenched glass. Significant photocatalytic activities were observed in as-quenched transparent glass. Photocatalytic activities were studied using the degradation of Resazurin as well as pharmaceutical 17 β-Estradiol under UV irradiation. Measurement of contact angle shows enhanced hydrophilicity with the increase in crystallization of the samples. Further, for as quenched 2Bi2O3-B2O3 glass ceramic, under UV irradiation, the water contact angle decreased from 92.7° to 39.5° and the sample surface transformed from hydrophobic to hydrophilic. Effective photocatalytic performance along with photoinduced hydrophilicity promotes 2Bi2O3-B2O3 glass cera...