Mechanical confinement or restricted degrees of freedom have been explored for its potential to enhance the performance of ferroelectric devices. It presents an easy and reversible method to tune the… Click to show full abstract
Mechanical confinement or restricted degrees of freedom have been explored for its potential to enhance the performance of ferroelectric devices. It presents an easy and reversible method to tune the response for specific applications. However, such studies have been mainly limited to uni- or bi-axial stress. This study investigates the effect of hydrostatic pressure on the ferroelectric behavior of bulk polycrystalline Pb0.99Nb0.02(Zr0.95Ti0.05)0.98O3. Polarization versus electric field hysteresis plots were generated as a function of hydrostatic pressure for a range of operating temperatures (298–398 K). The application of hydrostatic pressure was observed to induce anti-ferroelectric like double hysteresis loops. This in turn enhances the piezoelectric, energy storage, energy harvesting, and electrocaloric effects. The hydrostatic piezoelectric coefficient (dh) was increased from 50 pCN−1 (0 MPa) to ∼900 pC N−1 (265 MPa) and ∼3200 pCN−1 (330 MPa) at 298 K. Energy storage density was observed to improve...
               
Click one of the above tabs to view related content.