The magnetic behavior and MCE property of NdGa compound were studied in detail. According to the temperature dependence of magnetization (M-T) curve at 0.01 T, two sharp changes were observed at 20 K (TSR) and 42 K (TC), respectively, corresponding to spin reorientation and FM-PM transition. Isothermal magnetization curves up to 5 T at different temperatures were measured and magnetic entropy change (ΔSM) was calculated based on M-H data. Temperature dependences of –ΔSM for a field change of 0-2 T and 0-5 T show that there are two peaks on the curves corresponding to TSR and TC, respectively. The value of the two peaks is 6.4 J/kg K and 15.5 J/kg K for the field change of 0-5 T. Since the two peaks are close, the value of –ΔSM in the temperature range between TSR and TC keeps a large value. The excellent MCE performance of NdGa compound benefits from the existence of two successive magnetic transitions.