We combined an in situ biasing technique with phase-shifting electron holography, which can simultaneously achieve a high precision and high spatial resolution, to measure the electric potential, field, and charge density profiles across a GaAs p-n tunnel junction. A thin-film specimen was prepared by thinning one part of a bulk specimen using a cryo focused ion beam (FIB) system. We obtained precise electric potential profiles and successfully converted them into smooth electric field and charge density profiles without any fitting simulations. From the relationship between the applied voltage and measured height of the potential step across the p-n junction, the built-in potential of the p-n junction was determined to be 1.55 ± 0.02 V. The electric field profiles showed that the unbiased p-n junction had a depletion layer with a width of 24 ± 1 nm; the width increased to 26 ± 1 nm under a reverse bias of −0.3 V and decreased to 22 ± 1 nm under a forward bias of 0.5 V. Moreover, the charge density profiles indicated the presence of passivated dopants and/or trapped carriers even in the internal active layer of the specimen, with little damage introduced by FIB milling.We combined an in situ biasing technique with phase-shifting electron holography, which can simultaneously achieve a high precision and high spatial resolution, to measure the electric potential, field, and charge density profiles across a GaAs p-n tunnel junction. A thin-film specimen was prepared by thinning one part of a bulk specimen using a cryo focused ion beam (FIB) system. We obtained precise electric potential profiles and successfully converted them into smooth electric field and charge density profiles without any fitting simulations. From the relationship between the applied voltage and measured height of the potential step across the p-n junction, the built-in potential of the p-n junction was determined to be 1.55 ± 0.02 V. The electric field profiles showed that the unbiased p-n junction had a depletion layer with a width of 24 ± 1 nm; the width increased to 26 ± 1 nm under a reverse bias of −0.3 V and decreased to 22 ± 1 nm under a forward bias of 0.5 V. Moreover, the charge density profil...