LAUSR

The local structure around Er and Yb centre in ZnO favouring upconversion luminescence was studied using EXAFS (Extended X-ray absorption fine structure spectroscopy). Due to the ionic radii difference between Zn and Er, Yb ions, the dopants cannot replace Zn in the ZnO lattice properly. Er2O3 and Yb2O3 impurity phases are formed at the grain boundaries of ZnO. It is found that the local structure around the Er centre in ZnO is modified on annealing in air. The symmetry around both erbium and ytterbium reduces with increase in annealing temperature. Symmetry reduction will favour the intra-4f transition and the energy transitions causing upconversion luminescence. By fitting the EXAFS data with theoretically simulated data, it is found that the Er centre forms a local structure similar to C4ν symmetry which is a distorted octahedron. On annealing the sample to 1200 °C, all the erbium centres are transformed to C4ν symmetry causing enhanced upconversion emission. Yb centre has also been modified on anneali...