We report the influence of the AlN interlayer thickness (0-15 nm) on the photovoltaic properties of Al0.37In0.63N on Si heterojunction solar cells deposited by radio frequency sputtering. The poor junction… Click to show full abstract
We report the influence of the AlN interlayer thickness (0-15 nm) on the photovoltaic properties of Al0.37In0.63N on Si heterojunction solar cells deposited by radio frequency sputtering. The poor junction band alignment and the presence of a 2-3 nm thick amorphous layer at the interface mitigates the response in devices fabricated by direct deposition of n-AlInN on p-Si(111). Adding a 4-nm-thick AlN buffer layer improves the AlInN crystalline quality and the interface alignment leading to devices with a conversion efficiency of 1.5% under 1-sun AM1.5G illumination. For thicker buffers the performance lessens due to inefficient tunnel transport through the AlN. These results demonstrate the feasibility of using In-rich AlInN alloys deposited by radio frequency sputtering as novel electron-selective contacts to Si-heterojunction solar cells.We report the influence of the AlN interlayer thickness (0-15 nm) on the photovoltaic properties of Al0.37In0.63N on Si heterojunction solar cells deposited by radio frequency sputtering. The poor junction band alignment and the presence of a 2-3 nm thick amorphous layer at the interface mitigates the response in devices fabricated by direct deposition of n-AlInN on p-Si(111). Adding a 4-nm-thick AlN buffer layer improves the AlInN crystalline quality and the interface alignment leading to devices with a conversion efficiency of 1.5% under 1-sun AM1.5G illumination. For thicker buffers the performance lessens due to inefficient tunnel transport through the AlN. These results demonstrate the feasibility of using In-rich AlInN alloys deposited by radio frequency sputtering as novel electron-selective contacts to Si-heterojunction solar cells.
               
Click one of the above tabs to view related content.