The fatigue fracture behaviour and thermographic analysis of friction stir-welded (FSW) AZ31 was studied. It showed that fatigue fracture at the advancing side (AS). Heat-affected zone (HAZ) contained a greater fraction of coarse grains and a small amount of twins. The grains in the thermo-mechanically affected zone were smaller, indicating that grains may originate from incompletely dynamic recrystallisation during the FSW. The nugget zone is composed of equiaxed grains caused by the dynamic recrystallisation. During cyclic deformation, hysteresis loops from the AS of the FSW joints with the stain amplitude were higher than the retreating side of the FSW joints, the temperature of HAZ at AS is higher than other regions.