LAUSR

ABSTRACT Laser chemical vapor deposition (LCVD) was applied to prepare SmBa2Cu3O7-δ (SmBCO) superconductive films on single-crystalline LaAlO3 (100) substrates. The effect of oxygen partial pressure (P O2) on the crystal orientation, microstructure, and superconducting property of SmBCO film were investigated thoroughly. The results of X-ray diffraction (XRD) and Raman showed that the crystal orientation of SmBCO film was pure c -axis orientation at the P O2 of 200 Pa, and the a- axis orientation grains gradually emerged in SmBCO film with the increase of P O2. The deposition rate, critical temperature (T c), critical current density (J c) firstly increased and then decreased with the increase of P O2. At the P O2 of 200 Pa, the SmBCO film had smooth and dense surface, the lowest FWHM of φ-scan (1.1°), the highest T c (89.2 K) and J c (2.04 MA/cm2), which indicated that SmBCO superconductive films possessed excellent crystal structure and superconducting performance.