LAUSR

Room-temperature thermoelectric materials are important for converting heat into electrical energy. As a wide-bandgap semiconductor material, CuI has the characteristics of non-toxicity, low cost, and environmental friendliness. In this work, CuI powder was synthesized by a wet chemical method, then CuI film was formed by vacuum assisted filtration of the CuI powder on a porous nylon membrane, followed by hot pressing. The film exhibits a large Seebeck coefficient of 600 μV · K−1 at room temperature. In addition, the film also shows good flexibility (∼95% retention of the electrical conductivity after being bent along a rod with a radius of 4 mm for 1000 times). A finger touch test on a single-leg TE module indicates that a voltage of 0.9 mV was immediately generated within 0.5 s from a temperature difference of 4 K between a finger and the environment, suggesting the potential application in wearable thermal sensors.