LAUSR

A technique for directly growing two-dimensional (2D) materials onto conventional semiconductor substrates, enabling high-throughput and large-area capability, is required to realise competitive 2D transition metal dichalcogenide devices. A reactive sputtering method based on H2S gas molecules and sequential in-situ post-annealing treatment in the same chamber was proposed to compensate for the relatively deficient sulfur atoms in the sputtering of MoS2 and then applied to a 2D MoS2/p-Si heterojunction photodevice. X-ray photoelectron, Raman, and UV-visible spectroscopy analysis of the as-deposited Ar/H2S MoS2 film were performed, indicating that the stoichiometry and quality of the as-deposited MoS2 can be further improved compared with the Ar-only MoS2 sputtering method. For example, Ar/H2S MoS2 photodiode has lower defect densities than that of Ar MoS2. We also determined that the factors affecting photodetector performance can be optimised in the 8-12 nm deposited thickness range.