Purpose The purpose of this study is to improve the surface electrical conductivity and corrosion resistance of AISI430 stainless steel (430 SS) as bipolar plates for direct formic acid fuel cell (DFAFC). Design/methodology/approach The niobium diffusion layers have been successfully synthesized on 430 SS substrate by the plasma surface diffusion alloying technique under different diffusion alloying time. Findings The surface morphology of Nb-modified 430 SS prepared under the diffusion alloying time of 2 h is more homogeneous, relatively sleek and compact without surface micropore and other common surface blemishes. The potentiostatic and potentiodynamic polarization measurements manifest that Nb-modified 430 SS prepared under the diffusion alloying time of 2 h enormously ameliorate the corrosion resistance of bare 430 SS compared with other Nb-modified 430 SS samples and its corrosion current density is maintained at −1.4 µA cm−2 in simulated anodic environment of DFAFC (0.05 M H2SO4 + 2 ppm HF + 10 M formic acid at 50 °C). Originality/value The effect of diffusion alloying time on the corrosion resistance and surface conductivity of Nb-modified 430 SS has been carefully studied. The Nb-modified 430 SS samples prepared at the diffusion alloying time of 2 h have the best surface electrical conductivity and corrosion resistance in the simulated anodic environment of DFAFC.