LAUSR

Purpose The purpose of this paper is to investigate the resistivity of geopolymer cement with nano-silica additive toward acid exposure for oil well cement application. Design/methodology/approach An experimental study was conducted to assess the acid resistance of fly ash-based geopolymer cement with nano-silica additive at a concentration of 0 and 1 wt.% to understand its effect on the strength and microstructural development. Geopolymer cement of Class C fly ash and API Class G cement were used. The alkaline activator was prepared by mixing the proportion of sodium hydroxide (NaOH) solutions of 8 M and sodium silicate (Na2SiO3) using ratio of 1:2.5 by weight. After casting, the specimens were subjected to elevated curing condition at 3,500 psi and 130°C for 24 h. Durability of cement samples was assessed by immersing them in 15 wt.% of hydrochloric acid and 15 wt.% sulfuric acid for a period of 14 days. Evaluation of its resistance in terms of compressive strength and microstructural behavior were carried out by using ELE ADR 3000 and SEM, respectively. Findings The paper shows that geopolymer cement with 1 wt.% addition of nano-silica were highly resistant to sulfuric and hydrochloric acid. The strength increase was contributed by the densification of the microstructure with the addition of nano-silica. Originality/value This paper investigates the mechanical property and microstructure behavior of emerging geopolymer cement due to hydrochloric and sulfuric acids exposure. The results provide potential application of fly ash-based geopolymer cement as oil well cementing.