LAUSR

Purpose The purpose of this paper is to investigate the variables of the fused deposition modelling (FDM) process and improve their effect on the mechanical properties of acrylonitrile butadiene styrene (ABS) components reinforced with copper microparticles. Design/methodology/approach In the experimental approach, after drying the ABS granule, it was mixed with copper microparticles (at concentrations of 5%, 8% and 10%) in a single screw extruder to fabricate pure ABS and composite filaments. Then, by making the components by the FDM process, the tensile strength of the parts was determined through tensile strength tests. Taguchi DOE method was used to design the experiments in which nozzle temperature, filling pattern and layer thickness were the design variables. The analysis of variance (ANOVA) and signal-to-noise analysis were conducted to determine the effectiveness of each FDM process parameter on the ultimate tensile strength of printed samples. Following that, the main effect analysis was used to optimize each process parameter for pure ABS and its composite at different copper contents. Findings The study allows the layer thickness and filling pattern had the highest effects on the ultimate tensile strength of the printed materials (pure and composite) in the FDM process. Moreover, the results show that the ultimate tensile strength of the ABS composite containing 5% copper was nearly 12.3% higher than the pure ABS part. According to validation tests, the maximum error of experiments was about 0.96%. Originality/value In this paper, the effect of copper microparticles (as filling agent) was investigated on the ultimate tensile strength of printed ABS material during the FDM process.