Purpose This paper aims to investigate the effect of delayed water curing on the mechanical and microstructural properties of fly ash-based geopolymer paste-blended with Ground Granulated Blast Furnace Slag (GGBS) with different rest periods. Design/methodology/approach The blended geopolymer paste was composed of GGBS (15 per cent of the total weight) and the base material, Fly Ash (FA). The blended mix was activated by activator solution (Sodium hydroxide and Sodium silicate) containing 6 per cent Na2O of total base material. The effect of delayed water curing has been studied by gradually increasing the aging period (Rest Period) from 2 hours to 24 hours in the formation of activated outcome along with Calcium Silicate Hydrate (CSH). To analyze the mechanical and microstructural properties of the resultant blended geopolymer paste, compressive strength test, FESEM and XRD have been carried out. Moreover, a long-term durability test subjected to sulphate exposure has been performed to evaluate the durability of the designed sustainable geopolymer paste. Findings The present paper shows that the delayed water curing incorporates secondary heat input enhancing the partial polymer formation along with CSH. Slag-blended AAFA-based geopolymer paste is seen to exhibit quick setting property. Also, AAFA-based geopolymer paste samples subjected to longer rest period show early strength gain at a high rate under water curing as compared to those subjected to the shorter rest period. Originality/value To the best of authors’ knowledge, the effect of delayed water curing on the mechanical and microstructural properties of slag-blended AAFA-based geopolymer paste has not been studied before.