We report a potential method for the fabrication of Si-based Ge film with low threading dislocation (TD) density ( Click to show full abstract
We report a potential method for the fabrication of Si-based Ge film with low threading dislocation (TD) density (<105 cm−2) based on a low-temperature Ge/Si wafer bonding and smart cut technique. This method may replace the traditional epitaxial growth to solve the problems related to the TDs, high temperature, and high vacuum. A near-bubble-free Ge/Si bonded interface is achieved for the fabrication of Ge/Si p-i-n photodiodes. The insertion of amorphous Ge (a-Ge) has crystallized after Ge layer exfoliation, achieving a small FWHMXRD (96 arcsec) of the Ge peak. This determines the low dark current density (5.97 mA/cm2) and low ideality factor (1.19) of the Ge/Si p-i-n photodiode. The exfoliated Ge film suffers from in-plane compression strain due to the expansion of the H2 gas during the blistering process. Interestingly, the in-plane compression strain turns into tensile strain after high-temperature postannealing due to the faster shrinkage rate of Ge during cooling. The in-plane tensile strain leads to the increase in the responsivity of the photodiode. The responsivity of the photodiode at 1310 nm increases from 0.505 to 0.71 A/W and that at 1550 nm increases from 0.244 to 0.524 A/W after postannealing. More importantly, the redshift of the absorption edge of the Ge/Si photodiode (0.1 A/W at 1630 nm) is also observed. This implies that the wafer-bonded Ge/Si p-i-n photodiode can be comparable with the epitaxial one and can be used for optical communication in all wavelength division multiplexing bands, including the
               
Click one of the above tabs to view related content.