LAUSR

Data on the morphology and normal growth rate of the (110) and (001) faces, velocities of step motion, and slopes of dislocation hillocks on the (001) face of K2CoxNi1–x(SO4)2 · 6H2O crystals at different supersaturations of solutions with a Co/Ni ratio equal to 1: 1 or 1: 2 have been obtained using a Michelson interferometer. The morphology of the (110) faces is found to be the same for solutions of both compositions. Powerful dislocation sources with large Burgers vectors dominate on the (001) face. The morphology of the (001) surface is rougher than that of (110), especially in a 1: 2 solution at high supersaturation. The (110) faces grow more slowly as compared with (001). The kinetic coefficients of steps on the (001) face are identical in the 1: 1 and 1: 2 solutions. The influence of the kinetic and morphological characteristics of (001) faces on the single-crystal quality is analyzed.