Coatings on graphite that are stable to oxidation and based on the silicon–boron–zirconium boride composite containing from 5 to 50% of fibrous zirconium dioxide as a modifying dopant have been produced by the suspension–annealing method. A nonporous layer is formed at the zirconium dioxide content ranging from 5 to 15%, while a porous layer is formed at its 50% content. A glass-forming melt, as well as zirconium dioxide and silicate, is formed during thermal treatment as a result of the chemical reactions with the oxygen in air. The zirconium silicate content increases, along with the modifier’s concentration and temperature.