The Sc:Fe:Cu:LiNbO3 crystals were grown with Fe3+(0.3 wt.%), Cu2+(0.1 wt.%) and Sc3+(1 mol.%) by the Czochralski method with various [Li]/[Nb] ratios (0.946, 1.05, 1.20 and 1.38). The influence of the [Li]/[Nb] ratios on… Click to show full abstract
The Sc:Fe:Cu:LiNbO3 crystals were grown with Fe3+(0.3 wt.%), Cu2+(0.1 wt.%) and Sc3+(1 mol.%) by the Czochralski method with various [Li]/[Nb] ratios (0.946, 1.05, 1.20 and 1.38). The influence of the [Li]/[Nb] ratios on the defect structure of Sc:Fe:Cu:LiNbO3 crystals was analyzed by the UV-Visible spectra and IR transmission spectra. The spectra show that the absorption edge shift to the red with [Li]/[Nb] ratios enhancing. The Sc:Fe:Cu:LiNbO3 crystals with [Li]/[Nb] ratio of 1.05 is nearly stoichiometric. A new narrow OH− associated vibrational peak at 3505 cm−1 was revealed in Sc:Fe:Cu:LiNbO3 crystals with the ratio of [Li]/[Nb] = 1.38. It is attributed to the (ScNb2−)-(OH)−. The results show that the defect structure changes with the [Li]/[Nb] ratios variation.
               