One of the key figures for the success of proton exchange membrane fuel cells (PEMFCs) in automotive applications is lifetime. Damage of the cathode carbon support, induced by hydrogen/air fronts moving through the anode during start-up/shut-down (SUSD), is one of the lifetime limiting factors. In this study, we examine the impact of varying the temperature at which SUSD events take place, both experimentally and by a kinetic model. For MEAs with conventional carbon supports, the model prediction of carbon oxidation reaction (COR) currents as a function of temperature matches well with the temperature dependence of experimentally determined SUSD degradation rates (predicting ≈8-fold lower COR currents compared to ≈10-fold lower measured degradation rates at 5°C compared to 80°C). This, however, is not the case for MEAs with graphitized carbon supports, where a factor of ≈39 lower COR currents are predicted when decreasing SUSD temperature from 80 to 5°C, in contrast to the measured decrease by a factor of ≈10. As we will show, this is explained by a change of the governing degradation mechanism from predominantly carbon corrosion induced losses at higher temperature to predominantly voltage cycling induced platinum surface area losses near/below room temperature.