In this study, an attempt has been made to study the effect of alkali activator on the standard consistency and setting times of low calcium fly ash (FA) and ground granulated blast furnace slag (GGBS)- based sustainable geopolymer pastes. Different proportions of FA and GGBS were blended into mixes of geopolymer paste using sodium hydroxide (SH) and sodium silicate (SS) as alkaline activator solution (AAS). Tests on geopolymer pastes for consistency and initial and final setting times were carried out for three different SH : SS ratios of 1 : 1, 1 : 2, and 1 : 3 for both 2.5 M (molarity) and 5.0 M of SH concentration. While increasing the molarity of SH, both consistency and setting time decreased. For all the blended binder mix, the setting time decreases with an increase in the quantity of SS in the alkali activator solution. An increase in the amount of GGBS content in the geopolymer blended binder mix increases the consistency and decreases the setting time. For both 2.5 M and 5 M blended geopolymer mixes, a decrease in the percentage of GGBS and an increase in the percentage of FA increased the setting time. Microstructural studies such as X-ray fluorescence analysis (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FT-IR) analyses were carried out, and the results are presented. The FT-IR spectra for the blended binder mixes demonstrated the formation of geopolymerization and the presence of the functional groups.