LAUSR

We report a, to the best of our knowledge, new device fabrication process for 128-pixel linear arrays of InAs planar avalanche photodiodes, utilizing selective area implantation of Beryllium ions into epitaxially-grown InAs wafers. The pixels exhibited uniform avalanche gain and responsivity. Room temperature responsivity values at 1550 and 2004 nm wavelengths are 0.49 ± 0.017 and 0.89 ± 0.024 A/W, respectively. Reverse dark current-voltage and avalanche gain measurements were carried out at different temperatures (from room temperature to 150 K). At 200 K at -15 V reverse bias, the pixels exhibited an avalanche gain of 22.5 ± 1.18 and dark current density of 0.68 ± 0.48 A/cm2.